Effect of Bacillus and Pseudomonas biofilms on the corrosion behavior of AISI 304 stainless steel

24 March 2022, Version 1
This content is a preprint and has not undergone peer review at the time of posting.

Abstract

In this research work, the corrosion tendency of stainless steel (SS 304) caused by the Pseudomonas aeruginosa ZK (PA-ZK) and Bacillus subtilis S1X (BS-S1X) bacterial strains is investigated. The topographical features of the biofilms and SS304 substrate achieved after 14 days of incubation at 37 °C were examined by scanning electron microscopy (SEM). Fourier Transform Infrared Spectroscopic (FTIR) analysis of the extracellular polymer substance (EPS) was also carried out to estimate the chemical composition of the biofilm. Electrochemical Impedance Spectroscopy (EIS) and Tafel Polarization test methods were applied to understand the in-situ corrosion tendency of the SS304 in the presence of PA-ZK and BS-S1X strains. Compared to the biofilm produced by the PA-ZK, the EPS in the BS-S1X containing bacteria was porous and non-uniform as revealed in the SEM analysis. The improved hydrophobicity and uniformity of the PA-ZK containing biofilm retarded the corrosion of the underlying SS304 sample. Appreciably large resistance of the PA-ZK biofilm (~ 6.04 kΩ-cm2) and hindered charge transport (11.12 kΩ-cm2) was evident from the EIS analysis. In support of these results, a large cathodic Tafel slope (0.2 V/decade) and low corrosion rate (1.69 µA/cm2) were corroborated to the inhibitive properties of the PA-ZK containing biofilm. However, the formation of porous biofilm and non-homogeneity of the EPS layer produced by the BS-S1X bacteria enhanced localized corrosion as evident from the low charge transfer resistance, a high corrosion rate and formation of pits on the surface of SS304 were comparable to the surface features obtained after exposure to the controlled medium. These results highlighted the poor corrosion inhibitive properties of the BS-S1X bacteria compared to the PK-ZK bacterial strain.

Keywords

Biofilm
Biocorrosion
Bacterial strains
localized dissolution

Comments

Comments are not moderated before they are posted, but they can be removed by the site moderators if they are found to be in contravention of our Commenting Policy [opens in a new tab] - please read this policy before you post. Comments should be used for scholarly discussion of the content in question. You can find more information about how to use the commenting feature here [opens in a new tab] .
This site is protected by reCAPTCHA and the Google Privacy Policy [opens in a new tab] and Terms of Service [opens in a new tab] apply.